MECHANICAL PROPERTIES AND CORROSION RESISTANCE OF CAST NiAl ALLOYS WITH THE ADDITION OF Ti
DOI:
https://doi.org/10.7494/mafe.2015.41.1.29Keywords:
NiAl alloys, compression, corrosion resistanceAbstract
Results of compression and corrosion resistance tests of NiAl alloys with 1.0 and 2.0 wt.% of titanium are described. The compression tests conducted in a wide range of temperature and strain rate showed that increase of titanium content causes increase of brittleness at room temperature, while at higher temperatures an increase of hardness and strength is observed. The analysis of electrochemical corrosion resistance showed that the alloys containing Ti are characterized by considerable resistance to sulfuric acid VI, because the emerging titanium oxide prevents active solubilizing of the alloy. Besides, microstructure observations performed at various levels of deformation which allowed to identify mechanisms responsible for fracture of the studied alloys.
Downloads
References
. Darolia R., NiAl Alloys for high-temperature structural applications, JOM 43(3) 1991, 44–49
. Trinh D., Műller M.: Aluminides, 4H1609 Functional Materials, Project report, KTH 2002
. G. Frommeyer, R. Rablbauer, High Temperature Materials Based on the Intermetallic Compound NiAl Reinforced by Refractory Metals for Advanced Energy Conversion Technologies, Materials Technology, Steel Research International 79 (7) 2008, 507-513
. Pod red. Bojar Z. i Przetakiewicz W.: Materiały metalowe z udziałem faz międzymetalicznych, BEL Studio, Warszawa 2006.
. Ronald D. Noebe, Randy R. Bowman, Michael V. Nathal, The Physical and Mechanical Metallurgy of NiAl, Physical Metallurgy and processing of Intermetallic Compounds 1996, 212-296
. J.A. Hawk, D.E. Alman, Abrasive wear behaviour of NiAl and NiAl-TiB2 composites, Wear 225-229(1999), 544-556
. J. Colin, S. Serna, B. Campillo, O. Flores, J. Juárez-Islas, Microstructural and lattice parameter study of as-cast and rapidly solidified NiAl intermetallic alloys with Cu additions, Intermetallics 16(7)2008, 847–853
. J. Zhou, J.T. Guo, Effect of Ag alloying on microstructure, mechanical and electrical properties of NiAl intermetallic compound, Materials Science and Engineering A339 (2003) 166-174
. P. Hyjek, I. Sulima, P. Figiel, NiAl composite reinforced TiB2 ceramic particles, Innovative Manufacturing Technology 2013, The Institute of Advanced Manufacturing Technology, s.31-42.
. Shi-xiang Hou, Zong-de Liu, Dong-yu Liu, The study of NiAl–TiB2 coatings prepared by electro-thermal explosion ultrahigh speed spraying technology, Surface & Coatings Technology 205 (2011) 4562–4568
. P. Hyjek., P.Kurtyka., S. Wierzbiński, H. Krawiec, Odporność korozyjna kompozytów na osnowie stopu Al-Zn-Mg wzmacnianych cząstkami Al2O3, Composites 5(2005)2, 43-46
. A. Białobrzeski, E. Czekaj, M. Heller, Corrosive behaviour of aluminium and magnesium alloys processed by die casting technology, Archives of Foundry, 2(3)2002, 294-313
. A. Kmita, A. Janas, B. Hutera, Synthesis and evaluation of the structure of Ni3Al/C alloy, Metallurgy and foundry engineering 35(2)2009, 147-154
. P. Hyjek, I. Sulima, Microstructure and mechanical properties of Ni-Al-Ti-B alloy, Ores And Non-Ferrous Metals, 2015 (in press)