CORROSION RESISTANCE AND MICROSTRUCTURE OF STEEL AISI 316L AFTER COLD PLASTIC DEFORMATION
DOI:
https://doi.org/10.7494/mafe.2009.35.1.35Keywords:
corrosion resistance, austenitic steel, cold workingAbstract
In the paper, results of microstructure and hardness examination of cold-worked alloyed steel AISI 316L are presented. In addition, determined was corrosion resistance of the steel in the Ringer solution. Corrosion tests were performed after cold working with 10, 20, 30, 40 and 50% ratio. Potentiodynamic tests included recording polarisation curves as well as determining corrosive potential and corrosive current for various cold working ratios. Cross-sections of the specimens after corrosion tests were observed and analysed using a scanning microscope.
Downloads
References
Lechosław F., Krasicka-Cydzik E., Mstowski J., Zarzycki D.: Metalowe implanty kręgosłupowe. Systemy Dero: Rozwój technik operacyjnego leczenia kręgosłupa, 2-Sympozium, Zielona Góra (1997), 93-105
Przybyszewska-Doroś I., Okrój W., Walkowiak B.: Modyfikacje powierzchni implantów metalicznych, Inżynieria Biomateriałów (2005), 52-63
Jeleńkowski J., Borkowski T., Babul T.: Zmiany w strukturze strefy pośredniej podczas natryskiwania detonacyjnego, Inżynieria Materiałowa. 29 (2008) 6, 595-597
Babul T.: Połączenie powłoka-podłoże uzyskiwane metodą wybuchową i detonacyjną, Inżynieria Materiałowa. 20 (1999) 6, 623-627
Sińczak J., Kajtoch J., i in.: Procesy przeróbki plastycznej, Wyd. Nauk. AKAPIT, Kraków 2003
Tomaszow N.D.: Teoria korozji i ochrony metali. PWN, Warszawa 1962 (in Polish)
Krasicka-Cydzik E.: Badania wpływu obróbki powierzchniowej na odporność korozyjną stali implantowych. Archiwum Technologii Maszyn i Automatyzacji, 17 (1997) 1, 173-183
Ernst P, Newman R.C.: Pit growth studies in stainless steel foils, I. Introduction and pit growth kinetics. Corrosion Science 44 (2002), 927-941