THE INFLUENCE OF PHYSICAL AND CHEMICAL PARAMETERS OF MODIFIED WATER GLASS ON THE STRENGTH OF LOOSE SELF-SETTING SANDS WITH WATER GLASS
DOI:
https://doi.org/10.7494/mafe.2012.38.1.67Keywords:
viscosity, wettability, modification, water glassAbstract
An attempt of water glass modifying by 30% water bochmite Al(OH)O solution was undertaken. The flow curves were determined and the binder viscosity estimated from them. The quartz wettability by binders was determined by measuring the wetting angle θ changes with time. Strength properties of moulding sands with fractions of modified binders were verified by checking the tensile strength [formula] after various hardening times under environmental conditions. The [formula] value after 24 h of hardening was assumed for the analysis.
Downloads
References
Zych J:. Rola zagęszczenia w technologii formy opartej na masach ze szkłem wodnym lub spoiwem chemicznym, Przegląd Odlewnictwa, 21 (2005) 2, 88-97
Zych J:. Zachowanie się mas ze spoiwami chemicznymi w suchym powietrzu, Przegląd Odlewnictwa, 23 (2007) 9, 476-482
Zych J:. Optymalizacja technologii formy opartej na masach ze szkłem wodnym utwardzanym estrami, Przegląd Odlewnictwa, 21 (2005) 12, 782-792
Kuckui D. Nowe kierunki rozwoju mas ze szkłem wodnym oraz elektrofizycznych metod ich regeneracji, Przegląd Odlewnictwa 6 (1990) 1, 95-200
Ji-na W., Zi-tian K, Hua-feng W., Xuan-pu D., Nai-yu H:. An improved sodium silicate binder modified by ultra-fine powder materials, Ciuna Foundry, 4 (2007) 1, 26-30
Hutera B., Smyksy K., Lewandowski J.L., Drożyński D. Wybrane aspekty oznaczania zwilżalności osnowy przez materiały wiążące stosowane w masach formierskich, Archiwum Technologii i Automatyzacji, 23 (2003) 1, 63-70